group namePad printing silicone rubber
Min Order100 kilogram
brand nameHong Ye silicone rubber
modelHY918# silicone rubber for pad printing
payment methodT/T, L/C, Westem Union
update timeSat, 09 Nov 2013 12:42:11 GMT
Color any
Certifications ROHS.MSDS.SGS ISO
Min Order100 kilogram
Pad printing silicone rubber application:Pad printing silicone rubber
is mainly applicable to making pads for plastics toys, electroplating products, electronic toys, trademarks and irregular pattern printing.Pad printing pads is a carrier which transfer printing the patterns on the steel plate onto the toy products' surface.
Pad printing silicone rubber features:
Pad printing silicone rubber with the advantages of abrasion resistance, high temperature resistance, good printing effect, etc., which made of top-quality raw material due to adding American Dupont Teflon high-temperature resistance new material, is processed through high-temperature machining.
Pad printing silicone rubber datasheet:
Pad printing silicone rubber(HY-912)
Appearance:Yellow, red, green, white
Viscosity(CS):20000~25000
Hardness(A):28-30
Tensile strength (kgf/cm) ≥35
Tear-strength (kgf/cm) ≥24
Elongation break:(%)≥400
Retractility (%):≤0.3
Curing agent mixed rate(%):2-3
Operate time(min):30
Curing time(hours):2-4
Operation instruction for pad printing silicon rubber
Admixture amount of curing agent and silicon reaction:
1.Added with 1% of curing agent, silicone can still flow within 2.5 hours, mold can be released in6-8 hours.
2.Added with 2% of curing agent, silicone can still flow within 50 minutes to 1 hour, mold can be released in 2-3 hours.
3.Added with 3% of curing agent, silicone can still flow within 28-30 minutes, mold can be released in 1.5-2 hours
4.Added with 4% of curing agent, silicone can still flow within 10-15 minutes, mold can be released in 1-1.5 hours
5.Curing agent reaction rate is related with weather and temperature.Under 25 degree, they can be added according to the instruction or at double amount in winter or under subzero temperature.
(Note:Curing agent can not be added above the 4% maximum level and the normal proportion is 2%.If more than 4% is applied, the silicon will condensate too fast for normal usage).
Above is the mixing data for silicone and curing agent, the precise result of hundreds of times of our experiments.Provided that you arrange production according to our instruction, you are sure to manufacture first class products and maximize your profit this is not only the need of, but also our responsibility for and a satisfactory answer to our customers.We may not be the first, but we will try to be the best.The customers need is what we pursue!
Whatever you have any request or questions, pls feel free to email meor call me.
For get further information about our silicone product, PLS contact with Miss Rose
Tel: 0086-755-89948294
Mob:0086-18938867525
E-mail: hyjz(at)szrl(dot)net
Msn: ross1024(at)msn(dot)cn
Skype: LuoYan1012
网络文化经营许可证:浙ICP备14006100号-11 2007-2024 Tradevv.com. All rights reserved.