LED Liquid ge Silicone Sealant
- US $16.53
100 - 40,000 kilogram
- US $8.00
40,001 - 999,999 kilogram
group nameelectronic potting silicone rubber
-
Min Order100 kilogram
brand nameHong Ye silicone rubber
model9300
payment methodT/T, L/C, Westem Union
-
update timeSat, 09 Nov 2013 13:22:10 GMT
Paramtents
Classification Other Adhesives
Main Raw Material Silicone
Usage Construction,Fiber & Garment,Transportation,Woodworking
Appearance Transparent Fluid
Mixing Ratio 1:1
Viscosisty(after mixing) (cps) 600~1000
Operating Time (25℃ hr) 3
Curing Time (25℃ hr) 8
Curing Time (80℃ hr) 20
Hardness (Shore A) 0
Fire Resistance 94-V1
Shelf life 10~12month
MOQ 200kg
Packging & Delivery
Min Order100 kilogram
Briefing
Waterproofing, moisture-proof, mouldproof, dustproof, and fixed components;
Detailed
Features LED Liquid ge Silicone Sealant
Room temperature vulcanize, and easy to operate;
Maintain flexibility at a wide temperature range, and excellent insulation performance;
Waterproofing, moisture-proof, mouldproof, dustproof, and fixed components;
Resistance to Chemical dielectric, anti-yellowing, resistance to climate ageing.
Typical Application of LED Liquid ge Silicone Sealant
LED Liquid ge Silicone Sealant is suitable for bonded seal of electronic components, power module and control module, which requires waterproof and insulation. It can be broadly used for LED screen, Wind Power Generator, PCB substrate, etc.
Technical Parameters of LED Liquid ge Silicone Sealant
Features | Part A | Part B | |
Before Curing | Appearance | Transparent Fluid | Transparent Fluid |
Viscosisty(25°C cps) | 600±200 | 800±200 | |
Operation features | Mixing Ratio | 1:1 | |
Viscosisty(after mixing) (cps) | 600~1000 | ||
Operating Time (25°C hr) | 3 | ||
Curing Time (25°C hr) | 8 | ||
Curing Time (80°C hr) | 20 | ||
After Curing | Hardness (Shore A) | 0 | |
Thermal conductivity [W (m·k) ] | ≥0.2 | ||
Dielectric Strength(KV/mm) | ≥25 | ||
Permittivity (1.2MHz) | 3.0~3.3 | ||
Volume Resisivity (Ω·cm) | ≥1.0×1016 | ||
linear expansibility [m/(m·K)] | ≤2.2×10-4 | ||
Fire Resistance | 94-V1 | ||
TECHNICAL GUIDELINES
1, Pls put part A and part B in separate container and stir evenly before mixing the two part
together.
2, Weight Ratio: part A: part B = 1:1
3, Deaeration the mixture under 0.08 MPa for 3 minutes.
4, The temperature influences the curing time of 9301. When in too low temperature, we
suggest customers appropriately heat the mixture to accelerate vulcanization.
Warm Tips:
1.The following material may hinder the curing of the product, So pls apply after summary
experiment. When necessary, pls clean the application areas.
Condensation silicone which not completely cured or organic tin compounds
Sulphur, sulfide and sulfur rubber materials.
Amine compounds as well as contains the amine materials.
Pewters solder flux.
2. Should be sealed storage.The mixture should be used up at once, avoid causing waste.
3. Silicone belongs to non-dangerous goods, but keep away from mouth and eyes.
4. When it gets stratified after a period of storage, Please mix 9301 evenly before using, it
does not affect the performance.
PACKAGE
20Kg/pail (Part A10Kg + Part B10Kg)
SHELF LIFE AND TRANSPORTATION
1. Twelve(12) months from date of shipment when stored at 24C in original unopened
packages.
2. This kind of product is non-dangerous product, it can be transported as general
chemicals.
3. Products exceed the storage life should be confirmed normal before using.
Any questions about Silicone Rubber, Leah is at your service.
TEL: 086-755-89212382
FAX: 086-755-89948030
MOBILE: 086-189 3886 7561
Website: www(dot)szrl(dot)net
E-MAIL: hyji(at)szrl(dot)net
Skype: leahchou1214
QQ: 189 3886 7561
You need a product
You May Like
- Nearest port for product export
- Shenzhen, Guangzhou, Xiamen, Shanghai
- Delivery clauses under the trade mode
- FOB, CFR, CIF
- Acceptable payment methods
- T/T, L/C, Westem Union
- Export mode
- Export through agents