group nameelectronic potting silicone rubber
Min Order200 kilogram
brand nameHong Ye silicone rubber
modelHY-9055 silicon
payment methodL/C, T/T, Western Union, paypal
update timeThu, 14 Apr 2016 10:57:56 GMT
color: white
sample free
transport by sea
Certifications: RoHS.SGS ISO9001:2000
name liquid potting compound silicone
operating time adjusted
curing time adjusted
delivery time 5 days after payment
place of original GuangDong of China
Hardness any hardness
Weight1.28kg / kilogram
Min Order200 kilogram
Additional type heat conduction liquid potting compound silicon
Additional type heat conduction liquid potting compound silicon
HY 9055 could be applied to
- high powered electronics,
- DC/DC module and circuit board which requires heat dissipation and high temperature resistance.
-It can be broadly used for LED screen, Wind Power Generator, PCB substrate, etc.
Additional type heat conduction liquid potting compound silicon
HY 9055 is a kind of low viscosity, Inherent flame resistance, two components addtionecured potting silicon ith heat-conducting. It cures with both on room temperature and heated temperature. It has the feature of the higher temperature the faster of the curing time. It can be applied to electronic components for insulation, waterproofing, fixed and flame retardant. It mainly applied in electronic components surface with materials of PC(Poly-carbonate),PP,ABS,PVC, etc. and metal materials.
Additional type heat conduction liquid potting compound silicon
1, Pls put part A and part B in separate container and stir evenly before mixing the two part together.
2, Mixing Ratio: part A: part B = 1:1
3, Deaeration the mixture in vacuum pump under 0.08 MPa for 3-5 minutes.Then the mixture could be used for pouring.
4, Pls note that the thickness of the silicone affects the curing time. If the silicone used is a little thick,then the curing time will be a little longer.The temperature also affects the curing time.When in lower temperature, we suggest customers appropriately heat the mixture to accelerate vulcanization. With temperature of 80~100°C, the silicone will cure in 15 minutes; while in 25°C room temperature, the silicone will cure around 8 hours.
Additional type heat conduction liquid potting compound siliconNotes:
1.The following material may hinder the curing of HY 9055, So pls use after the test. When necessary, pls clean the application areas.
Organotin compound or Condensation silicone with organotin;
Sulphur, sulfide and sulfur rubber materials;
Amine compounds as well as contains the amine materials;
Pewters solder flux;
2. HY 9055 should be sealed storage.The mixture should be used up disposably to avoid causing waste.
3. HY 9055 belongs to non-dangerous goods, but keep away from mouth and eyes.
4. When it gets stratified after a period of storage, Please mix it evenly before using,which does not affect the performance.
Any questions, please feel free to contact Raemon:
SHENZHEN HONG YE JIE TECHNOLOGY CO., LTD
Website: www(at)szrl(dot)net
ADD: Liulian Shibi industrial, Pingdi town, Longgang district, Shenzhen, China
More information needed,Please feel free to contact Miss.Raemon:
E-mail: raemon(at)szrl.net
Tel: 18948315840
Skype: wendy.wen121
网络文化经营许可证:浙ICP备14006100号-11 2007-2024 Tradevv.com. All rights reserved.