200 - 1,000 kilogram
1,001 - 9,999 kilogram
group nameRTV-2 silicone rubber for molds making
Min Order200 kilogram
brand nameHong Ye silicone rubber
modelmolding silicone rubber
payment methodL/C, T/T, Western Union, cash
update timeWed, 13 Apr 2016 10:57:48 GMT
Sample Free
Certification: SGS,MSDS,RoHS
Hardness: 25-40 shore A
Mixing Ratio: 2-3%
Shelf life 12 month
Operating time (hour 25 0C ) 0.5
Elongation-break(%) 180-450
EINECS No: 39100000
Curing time(hour) 3-5
Curing agent: 3%for free charged
Weight1.28kg / kilogram
Min Order200 kilogram
liquid silicone rubber for artificial stone
1. Application for liquid silicone rubber for artificial stone :
Liquid Silicone Rubber is primarily intended for poly resin crafts, PU crafts, gypsum crafts, unsaturated resin crafts, lighting and candles crafts, plastic toy, stationery gifts crafts industry, a large statue Buddha, relievo furniture, furniture decorative materials, statues Buddha, artifacts copied, building decoration materials, large-scale cement mold, artificial fossils Factory, Europe component factory, simulation landscapes, animals and plants sculpture, sandstone crafts and so on.
2. Instruction for liquid silicone rubber for artificial stone:
Add curing agent of 2%-3% at the room temperature, the silicone rubber is still operational within 30 minutes, and in 2-3 hours.
1. Adding curing agent 1%, the silicone rubber can still be operated within 2.5 hours and can be Demoulded after 6-8 hours.
2. Adding curing agent 2%, the silicone rubber can still be operated within 50 minutes to 1 hour and can Be demoulded after 2-3 hours.
3. Adding curing agent 3%, the silicone rubber can still be operated within 28 - 30 minutes and can bedemoulded after 1.5-2 hours.
4. Adding curing agent 4%, the silicone rubber can still be operated within 10 - 15 minutes and can be demoulded after 1 -1.5 hours.
3.Standand datasheet of liquid silicone rubber for artificial stone :
Model | Color | Mixing ratio (%) | Operation Time (mins) | Demould | Hardness ( A0 ) | Tensile-strength (MPa) | Tear-strength (kN/m) | Dynamic Viscosity | Shrinkage | Elongation |
time | (mPa.s) | rate (%) | (%) | |||||||
( hrs) | ||||||||||
625# | white/translucent | 100;3 | 30-40 | 3 to 4 | 25±2 | 3.4 | 24±2 | 25000±2000 | ≤0.3 | 410 |
630# | white/translucent | 100;3 | 30-40 | 3 to 4 | 30±2 | 4 | 26±2 | 27000±2000 | ≤0.3 | 420 |
638# | white/translucent | 100;3 | 30-40 | 3 to 4 | 38±2 | 4 | 25±2 | 25000±2000 | ≤0.3 | 450 |
640# | white/translucent | 100;3 | 30-50 | 4 to 5 | 40±2 | 3.5 | 21±2 | 15000±2000 | ≤0.3 | 180 |
4.Steps of liquid silicone rubber for artificial stone:
Step One: Take 100g of part A and add 2g of part B and mix the silicone rubber and curing agent evenly.
Notes: Moulding silicon rubber is a kind of flowing liquid and it contains two parts. Part A is a kind of white flowing liquid and part B is the curing agent.
Step Two: vacuum pumping
Without exception, this step takes less than 10 minutes.
Note: The time for vacuum-pumping should be less than 3—5 mins , otherwise, once the silicone rubber has cross-link reaction during vacuumizing, it will not be operated.
Step Three: Brushing cast & Perfusion Molding operation
We are manufacturer specializing in molding silicone rubber, mold duplicating rubber for resin craft makers, special silicon for manual molding, shoe mold rubber, pad printing silicone, encapsulants and potting compound,addition cure liquid silicone,baby nipple silicone rubber ,lifecasting,food grade silicone rubber, trademark silicone rubber, HTV silicone rubber, lead-zinc alloy crafts silicone rubber, hot stamping silicone plate, hot stamping silicone roller, gross rubber, RTV-2 silicone rubber, silicone molds, silicone products,etc.
SHENZHEN HONG YE JIE TECHNOLOGY CO., LTD
Website: www(at)szrl(dot)net
ADD: Liulian Shibi industrial, Pingdi town, Longgang district, Shenzhen, China
More information needed,Please feel free to contact Miss.Raemon:
E-mail: raemon(at)szrl.net
Tel: 18948315840
Skype: wendy.wen121
网络文化经营许可证:浙ICP备14006100号-11 2007-2024 Tradevv.com. All rights reserved.