shoe mold silicone rubber with low shrinkage

FOB Price

US $7.85
200 - 1,000 kilogram
US $5.68
1,001 - 10,000 kilogram

group nameLiquid silicone rubber for insoles
Min Order200 kilogram
brand nameHong Ye silicone rubber
modelmolding silicone rubber
payment methodL/C, T/T, Western Union, cash and paypal
update timeTue, 12 Apr 2016 11:01:04 GMT

contact supplier

Paramtents

Sample Free
Certification: SGS,MSDS,RoHS
Hardness: 25-40 shore A
Mixing Ratio: 2-3%
Shelf life 12 month
Operating time (hour 25 0C ) 30-50mins
Elongation-break(%) 180-450
EINECS No: 39100000
Curing time(hour) 3-5 hrs
Curing agent: 3% for free charged

Packging & Delivery

Weight1.28kg / kilogram
Min Order200 kilogram

Briefing

1. Resistance to deformation
2. high-temperature
3. High reproduction times
4. Good tensile strength

Detailed

shoe mold silicone rubber with low shrinkage

1. shoe mold silicone rubber with low shrinkage application:

It is mainly used for shoe molds, sand casting, Shoe soles mold, sand casting,brushing mold,plaster models, simple products, products with non-complex patterns, as well as product models with stable size and non-deformation.

2. shoe mold silicone rubber with low shrinkage feature:

1. good aracteristics of easy-operation

2. Low shrinkage

3. Favorable tension

4. No deformation

5. High temperatureresistance, acid and alkali-resistance and ageing resistanc

3.Using Instruction of shoe mold silicone rubber with low shrinkage:

Component A is white flowing liquid and component B is the curing agent. For example, take liquid silicone rubber of 100g and add 2% curing agent for mixing evenly. After the liquid silicone rubber and the curing agent are completely mixed, put the liquid silicone rubber into a vacuum machine for deairing to remove the bubbles. After deaired, pouring the liquid silicone rubber into the product to be duplicated or into the mold frame.

4.Datasheet of shoe mold silicone rubber with low shrinkage:

Model	Color	Mixing ratio (%)	Pot life (mins)	Demould time ( hrs)	Hardness ( A0 )	Tensile-strength (kgf/cm2)	Tear-strength (kgf/cm)	Viscosity (cps)	Shrinkage rate (%)	Elongation (%)
218#	white	2-3	30-60	2~4	18-20	≥ 13	≥ 5	≤15000	≤0.3%	≥ 300

Model

Color

Mixing ratio (%)

Pot life (mins)

Demould

time

( hrs)

Hardness ( A0 )

Tensile-strength (kgf/cm2)

Tear-strength (kgf/cm)

Viscosity

(cps)