SUP9A Oil Hardened and Tempered Spring Steel Wires
group nameOil Hardened and Tempered Spring Steel Wires
-
Min Order1 metric ton
brand namefushun
modelSUP9A
payment methodL/C, D/A, D/P, T/T
-
update timeThu, 02 Apr 2020 14:26:34 GMT
Paramtents
Dameter 10-40mm
Delivery Condition Oil Hardened and Tempered
Surface Condition Black suface,Blasted
Packging & Delivery
Min Order1 metric ton
Briefing
Detailed
Products Details
1 High yield ratio, small spring residual deformation.
2 Stable performance: the difference of tensile strength in same coil is less than 60Mpa,which can extend the spring fatigue life.
3 The product rate after winding is high,which can reduce the cost. Oil quenching - tempering spring wire can not completely replace the cold-drawn spring wire. Especially the small size of the spring wire. Oil Hardened and Tempered spring wire is developed for the valve spring, suspension spring in fatigue resistance. And in order to achieve the best results, it should be combined with blasted process after winding. In recent years, with the improvement of the cognition level of this kind of product, this kind of product is gradually applied to clutch spring and car rigging.
Quality Standard
JIS G4801 2005 Spring Steels
Chemical Composition(%)
Steel Grade | C | Si | Mn | P | S | Cr |
SUP 9A | 0.56-0.64 | 0.15-0.35 | 0.70-1.00 | 0.030 max | 0.030 max | 0.70-1.00 |
Mechanical Properties(Quenched and Tempered Condition)(T=20°C if not differently stated)
Steel Grade | Tensile Strength Rm (Mpa) | Yield Strength Rp0.2 (Mpa) | Elongation A5 (%) | Area Reduction Ratio C (%) |
SUP 9A | 1225 min | 1080 min | 9 min | 20 min |
Heat Treatment
Steel Grade | Quenching Temperature (°C) | Media | Tempering Temperature (°C) |
SUP 9A | 830-860 | oil | 460-510 |
You need a product
You May Like
6YRS FUSHUN Metals
- Nearest port for product export
- Tianjin, Qingdao, Shanghai, Huangshi
- Delivery clauses under the trade mode
- FOB, CFR, CIF, CIP, CPT, DDP, DDU, DAF
- Acceptable payment methods
- T/T, L/C, D/P D/A