group nameAlloy Steel Bars
Min Order0 ton
brand namefushun
modelEN36C 832M13
payment methodL/C, D/A, D/P
update timeTue, 12 Oct 2021 13:57:59 GMT
OD range: 80-800mm
Delivery condition: hot forged+QT+Black or Bright surface
Surface condition: Black
OD tolerance +/- 1-5%
Min Order0 ton
Application of EN36C 832M13 1.6657:
EN36C 832M13 1.6657 can be used to make gear parts exposed to highest stresses and wear conditions. Typical components include gears, planet wheels, drive pinions, shafts, bushes and sleeves. Results in high core strength and excellent toughness in the components and is very suitable for parts with large diameter.
All Grades Comparison of EN36C 832M13 1.6657:
DIN | EN | ANFOR | BS |
1.6657 | 14NiCrMo13-4 | 16NCD13 | 832M13 / EN36C |
Quality Standard of EN36C 832M13 1.6657:
EN 10084 Case hardening steels
DIN17210 Case hardening steels
AS1444 Wrought alloy steels
Chemical Composition of EN36C 832M13 1.6657(%)
Steel Grade | C | Mn | Si | P | S | Cr | Ni | Mo |
14NiCrMo13-4 | 0.11-0.17 | 0.30-0.60 | 0.40 max | 0.025 max | 0.025 max | 0.80-1.10 | 3.00-3.50 | 0.20-0.30 |
Mechanical Properties of EN36C 832M13 1.6657: (T=20°C if not differently stated)
Process | Tensile Strength Rm (Mpa) | Elongation A5 (%) | Impact Value Kv (J) Room Temperature | Hardness (HB) |
SOFT ANNEALED | / | / | / | 217 max |
QUENCHED AND TEMPERED | 1230-1480 | 9 min | 35 min | 368-424 |
Heat treatment of EN36C 832M13 1.6657:
Soft Annealing: Heat EN36C to 825oC, cool slowly. This will produce a maximum Brinell hardness of 217.
Hardening: Harden from a temperature of 825-850oC, followed by oil or quenching.
Tempering:– After carburising and hardening, the steel is tempered between 140°C and 200°C as required.
For use in the non carburised heat treated condition, temper in accordance with properties required.