AISI 4140 G41400 SCM440 42CrMo4 1.7225 Alloy Steel Seamless Round Tube
group nameHollow Bars
-
Min Order1 piece
brand namefushun
model4140 G41400 SCM440 42CrMo4 1.7225
payment methodT/T, L/C, D/P D/A
-
update timeThu, 14 Oct 2021 14:30:23 GMT
Paramtents
OD 40-400MM
WT 5-30MM
Delivery condition QT
Surface condition peeled
Packging & Delivery
Min Order1 piece
Briefing
Detailed
4140 Seamless Tubing Are The Low Alloy Materials Used In The Industries. It Consists Of Manganese, Molybdenum And Chromium Chemical Components Which Adds Advanced Properties And Characteristics To AISI 4140 Material. Hence, Making It More Applicable For The Applications As Compared To Other Materials.The Molybdenum Chemical Component Used To Enhance The Resistivity Of The Material In High Elevated Temperatures.
Applications
Superior tensile strength and toughness
High strength to weight ratio
Easily heat treatable to a broad range of strength, machinability, and hardness.
Applications: aircraft components, hydraulic cylinders, rollers, structural apps, truck and automotive parts.
Chemical Composition (%)
Steel (UNS) | C | Si | Mn | P (≤) | S (≤) | Cr | Mo |
4140 (G41400) | 0.38-0.43 | 0.15-0.35 | 0.75-1.00 | 0.035 | 0.040 | 0.80-1.10 | 0.15-0.25 |
Steel | Tensile strength (Mpa) | Yield strength (Mpa) | Elongation in 50 mm, % | Reduction in area, % | Hardness (HB) | Sample diameter | Conditions |
AISI 4140 | 1020 | 655 | 17.7 | 46.8 | 302 | 25.4mm (1 inch) | Normalized at 870 °C |
655 | 414 | 25.7 | 56.9 | 197 | Annealed at 815 °C | ||
1075 | 986 | 15.5 | 56.9 | 311 | Water quenched from 845 °C & tempered at 540 °C |
Heat Treatment
AISI 4140 has enough carbon present to allow for adequate heat treatment. Recommended hardening procedures are to bring the steel up to 1,675 degrees Fahrenheit for normalization (removal of stress within the steel). After it cools properly, heat the steel to 1,550 degrees Fahrenheit before quenching it in oil. The toughness of the steel makes machining in its hardened form difficult. However, after annealing the steel at 1,600 degrees followed by a slow cooling, the steel is much softer and far easier to machine. It can then be heat-treated after machining to produce a hard, precise item.
You need a product
You May Like
6YRS FUSHUN Metals
- Nearest port for product export
- Tianjin, Qingdao, Shanghai, Huangshi
- Delivery clauses under the trade mode
- FOB, CFR, CIF, CIP, CPT, DDP, DDU, DAF
- Acceptable payment methods
- T/T, L/C, D/P D/A