1.2360 X48CrMoV8-1-1 Alloy tool steel with increased chromium content, average strength, high hardness, ductility and high abrasion resistance. Used for precision woodworking tools - knives, blades, cutters, handles for the paper, wood, pulp, and paper industries, as well as cold forming tools. The increased content of vanadium provides a high hardenability, which makes it possible to achieve hardness within the limits of 60 HRC.
Blanking tools, stamping tools, embossing tools, forming dies, press dies, die inserts, extrusion dies, reinforcements, cold extrusion tools, tube tools, cutting tools, industrial knives, wood chipping knives, veneer knives.
C(%) | Si(%) | Mn(%) | P(%) | S(%) | Cr(%) | Mo(%) | V(%) |
0.45-0.50 | 0.70-0.90 | 0.35-0.45 | Max 0.020 | Max 0.005 | 7.30-7.80 | 1.30-1.50 | 1.30-1.50 |
Proof strength | Tensile strength | Impact energy | Elongation at fracture | Reduction in cross section on fracture | As-Heat-Treated Condition | Brinell hardness(HBW) |
573(≥) | 122(≥) | 21 | 22 | 12 | Solution and Aging,Annealing,Ausaging,Q+T,etc | 311 |
Hardness in annealed condition <240 HB
Annealing in temperatures 835 - 865℃ cooling with furnace
Stress relief annealing at 650℃ cooling the furnace
Quenching at 1035 - 1070℃ with cooling in oil, salt bath or air
Tempering at temperatures 100 - 600℃