group nameAddition cure silicone rubber
Min Order200 kilogram
brand nameHong Ye silicone rubber
modelhongye silicone,620# ,625#,630# silicone rubber
payment methodT/T, L/C, Westem Union
update timeFri, 08 Nov 2013 17:23:27 GMT
Color White
Curing Agent 5%for free charged
Use For Molding
Certificated RoHS, Reach, MSDS,SGS.ISO9001:2008
Type silicone rubber
Appearance Fluid
Classification Chemical Auxiliary Agent
Min Order200 kilogram
RTV Mold Making Silicone For Prototyping (Addition Silicone Rubber)
Main application of RTV Mold Making Silicone For Prototyping (Addition Silicone Rubber)
· Rapid prototyping (urethane casting/silicone tooling/vacuum casting)
· GRC and Concrete moulding
· PU resin casting
· General Mouldmaking
· Superior manual mold design
Description of RTV Mold Making Silicone For Prototyping (Addition Silicone Rubber)
:
RTV mold making addition silicone are generally named as two-part addition silicone rubber that vulcanises at room temperature.Part A is a flowable liquid, part B is the curing agent(platinum catalyst). It features an exceptional fluidity ,good operability,excellent physical properties and very low shrinkage. The mixing ratio between Part A and Part B can be 10:1 or 1:1.
Main properties of RTV Mold Making Silicone For Prototyping (Addition Silicone Rubber) :
· almost nil shrinkage
· high chemical resistance to aggressive components of some types of resins
· good tear strength (this feature ensures higher resistance to wearing and shearing)
· high degree of precision in reproduction
· high dimensional stability over time and non-deformability
· high resistance to high temperatures and ageing (resit to -60-200°C)
· excellent non-stick effect
· environmental, odorless and nontoxic
E-series Translucent RTV-2 Addition silicone rubber standard datasheet (25°C)
(The mixing ratio of part A and part B can be adjusted to 1:1or 10:1)
Product | E-625 | E-642 |
Appearance | Translucent | Translucent |
Hardness(shore A) | 25±2 | 40±2 |
Mix ratio(A:B) | 1:1 | 10:1 |
Viscocity Part A(mPa.s) | 12000±2000 | 15000±2000 |
Viscocity Part B(mPa.s) | 1800±500 | 100±50 |
Tensile strength (MPa) | 6.7 | 7.6 |
Tear-strength (kN/m) | 23 | 22 |
Elongation(%) | 480 | 450 |
Density | 1.07 | 1.14 |
Pot life/working time (mins) | 30-40 | 30-40 |
Curing time/setting time (hrs) | 3-4hrs(25°C) 120-30mins(60°C) | 6-8hrs(25°C) 30-50mins(60°C) |
Shrinkage rate (%) | 0.1 | 0.1 |