HTV potting compound silicone/silicone rubber

FOB Price

US $12.80
200 - 40,000 kilogram
US $6.90
40,001 - 999,999 kilogram

group nameelectronic potting silicone rubber
Min Order200 kilogram
brand nameHong Ye silicone rubber
modelHY9060 silicon rubber
payment methodT/T, L/C, Westem Union
update timeFri, 08 Nov 2013 19:52:23 GMT

contact supplier

Paramtents

Viscosity (Pa.S) 2500~3500
Appearance Black Fluid/ White Fluid silicone rubber
Mixing Ratio 1:1
Hardness(Shore A) 60±5
Elongation at break (%) 450
Curing time(80°C mins) 20
Curing time (25°C hr) 8
MOQ 200KG
Packing 25kg/200kg
Brand Hong Ye silicone rubber

Packging & Delivery

Min Order200 kilogram

Briefing

HTV potting compound silicone, excellent tear strength, good resilience, good weatherability.

Detailed

Product Feature of HTV potting compound silicone

HTV potting compound silicone is a kind of low viscosity, Inherent flame resistance, two components addtion cured potting silicone with heatconducting. It cures with both on room temperature and heated temperature. It has the feature of the higher temperature the faster of the curing time. It can be applied to electronic components for insulation, waterproofing, fixed and flame retardant. The flame retardant UL94-V0 level can be achieved. It mainly applied in electronic components surface with materials of PC(Poly-carbonate),PP,ABS,PVC, etc. and metal materials.

Technical Parameters of HTV potting compound silicone

Features		Part A	Part B
Before Curing	Appearence	Black Fluid	White Fluid
	Viscosisty(25°Ccps)	3000±500	3000±500
Operation features	Mixing Ratio	1:1
	Viscosisty(after mixing) (cps)	2500~3500
	Pot life(r)	2
	Curing time (25°C hr)	8
	Curing time(80°C mins)	20
After Curing	Hardness(Shore A)	60±5
	Thermal conductivity [W(m·K)]	≥0.8
	Dielectric Strength(KV/mm)	≥25
	Permittivity(1.2MHz)	3.0~3.3
	Volume Resisivity(Ω·cm)	≥1.0×1016
	linear expansibility [m/(m·K)]	≤2.2×10-4
	Fire Resistance	94-V0

(Pls note: the above data for this product in 25 °C temperature, 55 percent humidity conditions, for reference. The accurate data is measured by customers to when using.)

TECHNICAL GUIDELINES of HTV potting compound silicone

1, Pls put part A and part B in separate container and stir evenly before mixing the two part together.

2, Weight Ratio: part A: part B = 1:1

3, Deaeration the mixture in vacuum pump under 0.08 MPa for 3-5 minutes.

4, The temperature influences the curing time of HY-9060#. When in too low temperature, we suggest customers appropriately heat the mixture to accelerate vulcanization. Suggested operation time and temperature. With temperature of 80~100°C, the silicone will cure in 15 minutes, while in 25°C room temperature, the silicone will cure around 8 hours.

PACKAGE of HTV potting compound silicone

20Kg/pail (Part A 10Kg + Part B10Kg)

SHELF LIFE AND TRANSPORTATION

1. Twelve(12) months from date of shipment when stored at 24C in original unopened packages.

2. This kind of product is non-dangerous product, it can be transported as general chemicals.

3. Products exceed the storage life should be confirmed normal before using.

Warm Tips about HTV potting compound silicone:
1.The following material may hinder the curing of the product, So pls apply after summary experiment. When necessary, pls clean the application areas.

l Condensation silicone which not completely cured or organic tin compounds

l Sulphur, sulfide and sulfur rubber materials.

l Amine compounds as well as contains the amine materials.

l Pewters solder flux.

2. Should be sealed storage.The mixture should be used up at once, avoid causing waste.

3. Silicone belongs to non-dangerous goods, but keep away from mouth and eyes.

4. When it gets stratified after a period of storage, Please mix 9060 evenly before using, it does not affect the performance.
HTV potting compound silicone/silicone rubber