group nameRTV-2 silicone rubber for molds making
Min Order100 kilogram
brand nameHong Ye silicone rubber
modelSilicone rubber 638#
payment methodL/C, T/T, Western Union
update timeThu, 21 Nov 2013 08:39:48 GMT
Color red/white
Application Mold making silicone rubber
Shelf life 12 months
Appearance Liqui
Purity 100%
Molding method Pouring / brushing
MOQ 100kgs
Sample Free
Package Vacuum packing
Min Order100 kilogram
Models of silicone rubber RTV for polyresin angel moulding
Model: 638# silicone rubber RTV for polyresin angel moulding
Appearance: white
Viscosity (cs): 25000
Hardness (A): 20-22
Tensile strength(kgf/cm2 ) ≥35
Tear strength (kgf /cm):≥25
Elongation break(%):≥500
Retractility (%):≤0.2
Curing agent mixed rate (%):2-3
Operate time (min): 30
Curing time (hours): 2-4
Model: 728#
Appearance: white
Viscosity (cs): 18000
Hardness (A): 25
Tensile strength(kgf/cm2 ) ≥35
Tear strength (kgf /cm):≥22
Elongation break(%):≥320
Retractility (%):≤0.2
Curing agent mixed rate (%):2-3
Operate time (min): 30
Curing time (hours): 2-4
Model: 788# silicone rubber RTV for polyresin angel moulding
Appearance: white
Viscosity (cs): 12000-15000
Hardness (A): 28-32
Tensile strength(kgf/cm2 ) ≥35
Tear strength (kgf /cm):≥20
Elongation break(%):≥470
Retractility (%):≤0.2
Curing agent mixed rate (%):2-3
Operate time (min): 30
Curing time (hours): 2-4
Features of silicone rubber RTV for polyresin angel moulding:
(1) Silicon rubber for pad printing with SGS and ROSH approval
(2) Curing agent arrange together as free charged
(3) In liquid form and in various colors
(4) With an exceptional fluidity and good operability.
(5)Temperature and deformation resistance as well as low shrinkage.
(6) High duplication times.
(7) Sample orders are available
(8) MOQ: 200KG
silicone rubber RTV for polyresin angel moulding instruction:
1. Component A is white flowing liquid and component B is the curing agent.
2. For example, take silicone rubber of 100g and add 2g curing agent for mixing evenly (silicone rubber and curing agent must be measured accurately).
3. After the silicone rubber and the curing agent are completely mixed, put the silicon into a vacuum machine for deairing to remove the bubbles.
4. After deaired, pouring the liquid silicone rubber into the product to be duplicated or into the mold frame. If you don't have vacuum machine, please add 1.2% or 1.5% curing agent so that the bubbles can bubble itself.
5. Since the less curing agent you add, the slower the mould will curdle, the bubbles will bubble out itself.
Any questions for silicone rubber RTV for polyresin angel moulding , pls feel free to contact Taylor:
Mob: +86-18938867522
Tel: + 86-755-89948006
E-mail: hyw(at)szrl(dot)net
Skype: taylordl828
Facebook: hyw(at)szrl(dot)net
网络文化经营许可证:浙ICP备14006100号-11 2007-2024 Tradevv.com. All rights reserved.