group nameRTV-2 silicone rubber for molds making
Min Order200 kilogram
brand nameHong Ye silicone rubber
modelHY625
payment methodT/T, L/C, Westem Union
update timeTue, 05 Nov 2013 12:13:06 GMT
color white
HS code 39100000
sample available
normal packing 25kgs per drum
delivery within 3 days
usage for mold making
MOQ 200KG
application for mold making
appearnce liquid
Min Order200 kilogram
liquid silicone material applications
liquid silicone material is primarily intended for poly resin crafts, PU crafts, PU resin crafts ,gypsum crafts ,unsaturated resin crafts, lighting and candles crafts ,plastic toy , stationery gifts crafts industry, a large statue Buddha, furniture, furniture decorative materials, statues Buddha, artifacts copied, building decoration materials, largescale cement mold, artificial fossils Factory, Europe component factory,
simulation landscapes, animals and plants sculpture, sandstone crafts and so on.
liquid silicone material description
liquid silicone material is white or red flowing liquid with general hardness of 22-50 shore A after curing. tin cured silicone rubber is a kind elastic silicon rubber mold which features with resistance to deformation, high-temperature, acid-alkali and expansion as well as high reproduction times, good tensile strength, tear strength and elongation.
FAQ. Why the liquid silicone material just can be reproduced for a few times?
It can be due to the following reasons:
a. Adding too much silicone oil in to silicon rubber. Silicon oil is an additive which destroies the molecular weight of silicone rubber and reduce the tension and tear strength.
b. Using the silicon rubber with a high hardness to make molds for small sized products with delicate and intricate designs and the silicon rubber with a low hardness to makes molds for large sized products with simple designs.
(Notes: we should choose the silicon rubber specifically according to the requirements of our products to avoid this problem.)
Datesheet of liquid silicone material .
Property | 625# | 630# |
Hardness (Shore A) | 25 | 30 |
Tensile strength, MPa | 3.1 | 3.6 |
Elongation @ break, % | 580 | 550 |
Tear Strength (N/mm) | 25 | 32.6 |
Linear shrinkage (%) | 0.3 | 0.3 |
Viscosity | 19000-22000 | 23000-25000 |
Color | Off White | Off White |
Mixing ration | 100:5 | 100:5 |
Pot life | 40 minutes | 30 minutes |
Cure time | 4-5 hours | 4-5 hours |
liquid silicone material Manufacturing instruction:
Add curing agent of 2%-3% at the room temperature, the liquid silicone material is still operational within 30 minutes, and in 2-3 hours.
1. Adding curing agent 1%, the liquid silicone material can still be operated within 2. 5 hours and can be demoulded after 6-8 hours.
2. Adding curing agent 2%, the liquid silicone material can still be operated within 50 minutes to 1 hour and can be demoulded after 2-3 hours.
3. Adding curing agent 3%, the liquid silicone material can still be operated within 30 minutes and can be demoulded after 1. 5-2 hours.
4. Adding curing agent 4%, the liquid silicone material can still be operated within 15 minutes and can be demoulded after 1-1. 5 hours.
Any questions of liquid silicone material, please feel free to contact Maggie :
TEL: 086-755-89948006
FAX: 086-755-89948030
MOBILE:086-18938867501
Website: www(dot)szrl(dot)net
E-MAIL: hysd(at)szrl(dot)net
网络文化经营许可证:浙ICP备14006100号-11 2007-2024 Tradevv.com. All rights reserved.