RTV silicone casting rubber

silicone casting rubber applications

silicone casting rubber      

is primarily intended for poly resin crafts, PU crafts, PU resin crafts ,gypsum crafts ,unsaturated resin crafts, lighting and candles crafts ,plastic toy , stationery gifts crafts industry, a large statue Buddha, furniture, furniture decorative materials, statues Buddha, artifacts copied, building decoration materials, largescale cement mold, artificial fossils Factory, Europe component factory, 

simulation landscapes, animals and plants sculpture, sandstone crafts and so on.

silicone casting rubber description

silicone casting rubber is white or red flowing liquid with general hardness of 22-50 shore A after curing. tin cured RTV silicone rubber  is a kind elastic silicon rubber mold which features with resistance to deformation, high-temperature, acid-alkali and expansion as well as high reproduction times, good tensile strength, tear strength and elongation.

FAQ. Why the silicone casting rubber just can be reproduced for a few times?

It can be due to the following reasons: 

a. Adding too much silicone oil in to silicon rubber. Silicon oil is an additive which destroies the molecular weight of silicone rubber and reduce the tension and tear strength.

b. Using the silicon rubber with a high hardness to make molds for small sized products with delicate and intricate designs and the silicon rubber with a low hardness to makes molds for large sized products with simple designs. 

(Notes: we should choose the silicon rubber specifically according to the requirements of our products to avoid this problem.)

Datesheet of  silicone casting rubber .

The proportions and reactions of the curing agent and the silicon as follows

a. Adding curing agent 1%, The  silicone casting rubber can still be operated within 2.5 hours and can be demoulded after 6-8 hours.

b. Adding curing agent 2%, Thesilicone casting rubber can still be operated within 50 minutes to 1 hour and can be demoulded after 2-3 hours.

c. Adding curing agent 3%,  The  silicone casting rubber can still be operated within 28 - 30 minutes and can be demoulded after 1.5-2 hours.

d. Adding curing agent 4%,  The silicone casting rubbercan still be operated within 10 - 15 minutes and can be demoulded after 1 -1.5 hours