Additional curing silicone rubber for mold making

FOB Price

US $10.88
200 - 40,000 kilogram
US $7.69
40,001 - 999,999 kilogram

group nameAddition cure silicone rubber
Min Order200 kilogram
brand nameHong Ye silicone rubber
modelHY-E630 Silicone
payment methodT/T, L/C, Westem Union
update timeFri, 08 Nov 2013 16:48:21 GMT

contact supplier

Paramtents

Certifications RoHS.MSDS.SGS ISO9001:2000
HS CODE 39100000
MOQ 200kgs
packing 200kgs/drum
feature liquid

Packging & Delivery

Min Order200 kilogram

Briefing

1.light viscosity, pourable effort
2.platinum curing
3.good tension and tear strength
4.high reproduction times

Detailed

Additional curing silicone rubber Features

Additional curing silicone rubber is mainly used for metallic arts & crafts, baby nipples, cake, candy food grade products mold making, medical catheter and so on. It is nontoxic and with very low shrinkage.

Main features of Additional curing silicone rubber

Low Viscosity, good operability

exceptional fluidity

good temperature

solvent resistance

insulation properties

excellent tensile and tear strength, as well as good elasticity.

Using Instructions of Additional curing silicone rubber

Applicable to the injection molding process
Mixing component A with B evenly according its mix ratio, it is ready for use after degassing, it cures by heating up the temperature when pouring into the mold.
The curing time is subject to the temperature, short time will be required under high temperature, long time will be required while the product with large thickness.

Model	E615	E620	E625	E630	E635
Appearance	Translucent	Translucent	Translucent	Translucent	Translucent
Mixing Ratio	1: 1	1: 1	1: 1	1: 1	1: 1
OperateTime(Mins25° C)	2~3	2~3	2~3	2~3	2~3
CuringTime (Mins 25° C)	30	30	30	30	30
Hardness (A° )	15± 2	20± 2	25± 2	30± 2	35± 2
Density ( g/cm 3 )	1.08	1.08	1.08	1.08	1.08
Viscosity (CS) (Part A)	10000 ± 2000	20000 ± 2000	22000 ± 2000	23000 ± 2000	26000 ± 2000
Viscosity(CS)(Part B)	5000 ± 500	5000 ± 500	4000 ± 500	5000 ± 500	5000 ± 500
Viscosity (CS) (After mixed)	12000 ± 2000	12000 ± 2000	10000 ± 2000	15000 ± 2000	16000 ± 2000
Tensile-strength( kgf /cm 2 )	35± 5	46± 5	44± 5	47± 5	48± 5
Tear-strength (kgf /cm )	10± 2	11± 2	12± 2	12± 2	11± 2
Elongation-break(%)	430 ± 50	460 ± 50	490 ± 50	420 ± 50	410 ± 50
Retractility(%)	≤ 0.1	≤ 0.1	≤ 0.1	≤ 0.1	≤ 0.1