group nameAddition cure silicone rubber
Min Order200 kilogram
brand nameHong Ye silicone rubber
modelHY-E625# silicone for shoe soles
payment methodT/T, L/C, Westem Union
update timeFri, 08 Nov 2013 17:08:54 GMT
color translucence
Export Markets worldwide
Group Addition silicone rubber
Standard ISO9001, SGS,FDA
HS Code 39100000
samples free
shelf life 12 month
mix ratio 1:1
status liquid
grade food grade
Min Order200 kilogram
Addition Curing Silicon Rubber (HY-E625)
Addition Curing Silicon Rubber application:
E625 is a kind of Addition Curing Silicon Rubber for choclate mold. It's liquid with moderate viscosity and can be poured and brushed. The mold made out of the silicone and curing agent, which with high temperature up to 250-300° C, has dimension stability, low linear shrinkage. It's a two-component material with mixing ratio of 1: 1, and it's used for soft mold making, etc.
OPERRATING INSTRUCTION of Addition Curing Silicon Rubber for choclate mold:
1. Stir part A and part B with right mixing ratio (1: 1) evenly. And get the mixture for vacuum-pumping. (If there is no vacuumize, you can just pour the mixture slowly from the corner so that less bubbles caused)
2. Enclose the product (the original model) with four plastic plates or wooden plates.
3. Clean your products and brush a layer of release agent (detergent or soap water) on your product.
4. Pour the mixture with correct mixing ratio into the model frame.
After about 2-4 hours, when the silicone cured, get out the original model, and there you get a finished addition cured silicone mold.
Model | E615 | E620 | E625 |
Appearance | Translucent | Translucent | Translucent |
Mixing Ratio | 1: 1 | 1: 1 | 1: 1 |
OperateTime(Mins25° C) | 2~3 | 2~3 | 2~3 |
CuringTime (Mins 25° C) | 30 | 30 | 30 |
Hardness (A° ) | 15± 2 | 20± 2 | 25± 2 |
Density ( g/cm 3 ) | 1.08 | 1.08 | 1.08 |
Viscosity (CS) (Part A) | 10000 ± 2000 | 20000 ± 2000 | 22000 ± 2000 |
Viscosity(CS)(Part B) | 5000 ± 500 | 5000 ± 500 | 4000 ± 500 |
Viscosity (CS) (After mixed) | 12000 ± 2000 | 12000 ± 2000 | 10000 ± 2000 |
Tensile-strength( kgf /cm 2 ) | 35± 5 | 46± 5 | 44± 5 |
Tear-strength (kgf /cm ) | 10± 2 | 11± 2 | 12± 2 |
Elongation-break(%) | 430 ± 50 | 460 ± 50 | 490 ± 50 |
Retractility(%) | ≤ 0.1 | ≤ 0.1 | ≤ 0.1 |