group nameAddition cure silicone rubber
Min Order100 kilogram
brand nameHong Ye silicone rubber
modelHY-620
payment methodT/T, L/C, Westem Union
update timeFri, 08 Nov 2013 18:15:45 GMT
color white/ off-white/ blue/ red
HS. Code 39100000
Purity 100%
Appearance Liquid
Application silicone rubber for tire molds
Sample Free
Catalyst 4% free of charged
MOQ 100KGS
Molding method Pouring , brushing
Certification SGS, RoHS, MSDS, FDA, REARCH, ISO9001:2000
Min Order100 kilogram
Non-deformation/ low shrinkage/silicone rubber for tire molds
Non-deformation/ low shrinkage/silicone rubber for tire molds Description
Non-deformation/ low shrinkage/silicone rubber for tire molds is generally named two-components silicone rubber, Part A and part B. It features an exceptional fluidity and good operability. The mixing ratio is 1:1 (10:1),mainly be suitable for making molds application.
non-deformation/ low shrinkage/silicone rubber for tire molds Typical Applications
non-deformation/ low shrinkage/silicone rubber for tire molds could be mainly used for making concrete stones, wax molds, PU molds, resin molds, gypsum casting, candle molding and chocolate , candy and any other FDA food product mold making,prototyping etc.
Non-deformation/ low shrinkage/silicone rubber for tire molds is has been used for years to make tire pattern molds .
non-deformation/ low shrinkage/silicone rubber for tire molds Characteristics
*low shrinkage (less than 0.1% )
*high tensile and tear strength with high copy times
*easy for operation (mixing ratio at 1:1 /10:1)
*very good flow and easy for pouring operation
*Fast and non-shrink cure at room temperature which can be accelerated considerably by the application of heat
Non-deformation/ low shrinkage/silicone rubber for tire molds Technical Parameters
Product | E-620 |
Appearance | Translucent |
Hardness(shore A) | 20±2 |
Mix ratio(A:B) | 1:1/10:1 |
Viscocity Part A(mPa.s) | 23000±2000 |
Viscocity Part B(mPa.s) | 3500±500 |
Tensile strength (kgf/cm2) | 45±5 |
Tear-strength (kN/m) | 20±2 |
Elongation(%) | 500±50 |
Pot life/working time (mins) | 30-40 |
Curing time/setting time (hrs) | 3-4hrs(25°C) 110-20mins(60°C) |
Shrinkage rate (%) | 0.1 |
(Please note: the above data for this product in 25°C temperature, 55percent humidity conditions, for reference. The accurate data is measured by customers when using.)
Non-deformation/ low shrinkage/silicone rubber for tire molds Notice
As our E-series silicone is platinum cure silicone , which is very easy to cause
cure inhibition , so pls do remember thoroughly clean the model and tool before
operation . Besides , pls avoid the liquid E-series silicone contact or mix with the
following material , otherwise the silicone won’t be cured :
1. Liquid condensation silicone ( condensation silicone not completely cured or organic
tin compounds )
2 .Sulphur, sulfide and sulfur rubber materials.
3. Amine compounds as well as contains the amine materials.
4 .Pewter solder flux.
Non-deformation/ low shrinkage/silicone rubber for tire molds Operation instruction
1. Pls clear the model and tool totally before operation to prevent cure inhibition.
2.Weigh the two part correctly by electronic weight in two separate container .
3. Mixing the two part in 1:1/10:1 and stir part A and part B evenly in 2-3 minutes .
4.And get the mixture for vacuum-pumping for de-air the bubble in around 2-3 minutes . (If there is no vacuum machine, pls pour the mixture carefully and slowly down the side of the mold frame so that less bubbles caused)
5. Enclose the product (the original model) with four plastic plates or wooden plates.
6. Clean your products and brush a layer of release agent(detergent or soap water) on
your product.
7. Pour the vacuumed mixture into the model frame from the side of the mold frame .
More details of non-deformation/ low shrinkage/silicone rubber for tire molds, pls feel free to contact Ms Taylor:
Tel:086-755-89212380
Mob:0086-18938867522
Skype: taylordl828
网络文化经营许可证:浙ICP备14006100号-11 2007-2024 Tradevv.com. All rights reserved.