200 - 40,000 kilogram
40,001 - 999,999 kilogram
group nameRTV-2 silicone rubber for molds making
Min Order200 kilogram
brand nameHong Ye silicone rubber
modelliquid silicone rubber
payment methodL/C, T/T, Western Union, paypal and cash
update timeWed, 30 Mar 2016 15:02:07 GMT
Hardness(shore A) 25±2
MOQ 200kg
Tensile strength (kgf/cm2) 50±5
Viscocity Part B(mPa.s) 23000±2000
Color Any color
Viscocity Part A(mPa.s) 23000±2000
Pot life/working time (mins) 30-40
Features liquid
Shrinkage rate (%) 0.1
Mix ratio(A:B) 1:1/10:1
Weight1.25kg / kilogram
Min Order200 kilogram
liquid silicone rubber addition cured plaster molds for statues
Description of liquid silicone rubber addition cured plaster molds for statues
HY- E series addition molding silicone is generally named two-components silicone
rubber, Part A and part B. It features an exceptional fluidity and good operability.
The mixing ratio is 1:1 (10:1),mainly be suitable for making molds application.
Typical Applications of liquid silicone rubber addition cured plaster molds for statues
HY- E series addition molding silicone could be mainly used for making concrete
stones, wax molds, PU molds, resin molds, gypsum casting, candle molding and
chocolate , candy and any other FDA food product mold making, prototyping etc.
Characteristics of liquid silicone rubber addition cured plaster molds for statues
*low shrinkage (less than 0.1% )
*high tensile and tear strength with high copy times
*easy for operation (mixing ratio at 1:1 /10:1)
*very good flow and easy for pouring operation
*Fast and non-shrink cure at room temperature which can be accelerated considerably by the application of heat
Technical Parameters of liquid silicone rubber addition cured plaster molds for statues
Model | E-625# |
Appearance | Translucent |
Mixing Ratio | 1:1 or 10:1 |
Viscosity part A (Mpa.s) | 20000±2000 |
Viscosity part B (Mpa.s) | 3500±1000 |
Viscosity mixed(Mpa.s) | 8000 ±2000 |
Operating time ( Mins 25C) | 20-40mins |
Curing time ( Hrs 25C) | 2~5hrs |
Hardness (A°) | 25±2 |
Tensile-strength(kgf /cm2 ) | 60±5 |
Tear-strength (Kgf/cm ) | 12±2 |
Elongation-break(%) | 300±20 |
Retractility(%) | ≤0.1 |
(Please note: the above data for this product in 25°C temperature, 55percent humidity conditions, for reference. The accurate data is measured by customers when using.)
OPERRATING INSTRUCTION for liquid silicone rubber addition cured plaster molds for statues:
1.Stir part A and part B with right mixing ratio evenly. (E630# is 1:1) and get the mixture for vacuum-pumping.(If there is no vacuumizer,you can just pour the mixture slowly from the corner so that less bubbles caused).2.Enclose the product (the original model) with four plastic plates or wooden plates.
3. Clean your products and brush a layer of release agent(detergent or soap water) on your product.
4.Pour the mixture with correct mixing ratio into the model frame. After about 2-4 hours, when the silicone cured, get out the original model, and there you get a finished addition cured silicone mold .
SHELF LIFE of liquid silicone rubber addition cured plaster molds for statues:
Twelve (12) months from date of shipment when stored at 24°C in original unopened packages.
PACKAGE for liquid silicone rubber addition cured plaster molds for statues:
Packed in clean 25kg/pail, 200kg/pail.