100CrMn6 1.3520 High Carbon-Chromium Bearing Steel Round Bar
group nameBearing Steel Bar
-
Min Order1 piece
brand namefushun
model100CrMn6, 1.3520
payment methodL/C, T/T
-
update timeMon, 22 Jun 2020 11:47:54 GMT
Paramtents
Diameter 20-180mm
Similar steel grades 100CrMn6, 1.3520
Delivery condition hot rolled+ spheroidizing annealing
Surface condition black, bright
Packging & Delivery
Min Order1 piece
Briefing
Detailed
Introduction:
Quality Standard:
All Grades Comparison:
Material No. 1.3520; EN 100CrMn6
Chemical Composition(%):
C | Si | Mn | P | S | Cr | Ni | Cu |
0.90-1.05 | 0.50-0.70 | 1.00-1.20 | 0.030 max | 0.025 max | 1.40-1.65 | 0.30 max | 0.30 max |
Heat treatment:
l NORMALIZING: Normalizing temperature: 860-900℃.
l SOFT ANNEALING: Heat to 760-800℃, cool slowly in furnace. This will produce a maximum Brinell hardness of 217.
l STRESS RELIEVING: Stress relieving to remove machining stresses should be carried out by heating to approx. 650℃, holding for 1-2 hours at heat, followed by air cooling. This operation is performed to reduce distortion during heat treatment.
l HARDENING: Harden from a temperature of 830-890℃ followed by oil quenching. Hardness after quenching is approx. 64 HRC.
l TEMPERING: Tempering temperature: 150-180℃.
You need a product
You May Like
6YRS FUSHUN Metals
- Nearest port for product export
- Tianjin, Qingdao, Shanghai, Huangshi
- Delivery clauses under the trade mode
- FOB, CFR, CIF, CIP, CPT, DDP, DDU, DAF
- Acceptable payment methods
- T/T, L/C, D/P D/A