304L Stainless Steel Spring Wires
group nameStainless Steel Spring Wires
-
Min Order1 metric ton
brand namefushun
model304L
payment methodL/C, D/A, D/P, T/T
-
update timeThu, 02 Apr 2020 10:16:42 GMT
Paramtents
Diameter 0.1-5mm
Tolerance +/- 0.01mm
Delivery Condition Cold Drawn Only,Annealed
Surface Condition Smooth,Soap-coated,Misty-gray and Bright surface
Packging & Delivery
Min Order1 metric ton
Briefing
Detailed
Introduction
The corrosion resistance of 304L stainless steels removes the requirement for any additional protective coatings making them the ideal material for springs operating in a range of corrosive conditions, high temperatures and in locations where maintenance and replacement are difficult.
Products Details
1 Excellent quality, high cost performance, suitable for manufacturing precision springs
2 Excellent microstructure, durable, can be widely used in automotive, office equipment and household appliances
3 Market-oriented, adhere to using of high-quality imported materials and Baosteel materials
4 Size range: Diameter 0.1-5.00mm
5 Delivery condition: Cold Drawn Only,Annealed
6 Surface condition: Smooth,Soap-coated,Misty-gray and Bright surface
Quality Standard
ASTM A580 2006 Standard Specification for Stainless Steel Wire
Chemical Composition(%)
Steel Grade | C | Si | Mn | P | S | Cr | Ni | N |
304L | 0.03max. | 1.00max. | 2.00max. | 0.045 max | 0.030 max | 18.0-20.00 | 8.0-12.0 | 0.10max. |
Mechanical Properties(Cold finished)
Steel Grade | Tensile Strength (Mpa) | Yield Strength (Mpa) | Elongation (%) | Area Reduction Ratio C (%) |
304L | 620 min | 310 min | 30 min | 40 min |
Mechanical Properties(Annealed)
Steel Grade | Tensile Strength (Mpa) | Yield Strength (Mpa) | Elongation (%) | Area Reduction Ratio C (%) |
304L | 485 min | 170 min | 35 min | 50 min |
You need a product
You May Like
6YRS FUSHUN Metals
- Nearest port for product export
- Tianjin, Qingdao, Shanghai, Huangshi
- Delivery clauses under the trade mode
- FOB, CFR, CIF, CIP, CPT, DDP, DDU, DAF
- Acceptable payment methods
- T/T, L/C, D/P D/A