Silicone rubber for trademark

Silicone rubber for trademark Standard Datasheet:

Typical curing Condition:170℃×5mins, prolong or shorten the curing time appropriately according to the thickness and size of the product during actual use.

Silicone rubber for trademark Using Instructions: The mixing proportion of HY-966A and HY-966B is 10:1. Mix component A and component B sufficiently and evenly according to the mixing proportion before use. The process of vacuum-pumping is also needed.

Note: The series of products must not be in contact with organisms like N, P, S, etc., ionic compounds like Hg, Bi, As, etc., and alkynes, vinyl compounds, etc. to avoid the situation at the products can not be cured due to platinum catalyst poisoning. The products particularly can not be in contact with PVC which contains lead causing catalyst poisoning. Some organic pigment also can slow down the curing time or cause uncured .
After HY-966A and HY-966B are mixed, the silicone rubber must be used up within 4 hours, otherwise the cross-linking and curing arises to lose effectiveness. In case of a higher surrounding temperature, more attention should be paid.

Instruction: Typical data can not be directly used for actual production guidance. Please contact us for details.
Package:General packages of HY-966 and HY-967 products is in 5kg per can, 20kg per pail and 200kg per barrel.
Precautions: The products can be transported as safety and non-hazardous goods since they are noninflammable with resistance to a high temperature above 300℃.